TheBlondeFella · 07-22-2013, 12:02 PM

Just wondering if a repaired cracked wheel will last if it's been repaired by a decent repairer?

Part of me is thinking that the wheel should actually be stronger around the weld as more metal has been addesd but the other part is thinking that once a wheel is cracked it will all ways have a weak spot in that area.

Any ideas?

VMRWheels · 07-22-2013, 02:46 PM

The crack is likely to come back at some point or another.

spiike32 · 07-22-2013, 04:24 PM

A more detailed answer is it depends.

If the crack is parallel to how the wheel is spinning (like on the barrel, then it should not be welded. Also if there is more than 1 crack it should not be welded.

If the crack is on the barrel and crosses the 90* flange then the crack can be opened up, end of the crack drilled out so it doesn't keep cracking, and welded. Some say integrity is just as strong some say it is not. Real world scenario: most likely it will be just fine.... just ugly because you can see the weld beads.

If you track and put the wheels to harsher stresses than normal use.. I would not weld them.

junitos · 07-22-2013, 04:42 PM

Not very long

07-22-2013, 12:02 PM	#1
TheBlondeFella First Lieutenant 40 Rep 386 Posts Drives: E93 320i M Sport Join Date: Jun 2013 Location: Surrey, UK iTrader: (3)	Reparied Cracked Wheels - Will They Last? Just wondering if a repaired cracked wheel will last if it's been repaired by a decent repairer? Part of me is thinking that the wheel should actually be stronger around the weld as more metal has been addesd but the other part is thinking that once a wheel is cracked it will all ways have a weak spot in that area. Any ideas?
	Appreciate 0 Tweet Quote

07-22-2013, 02:46 PM	#2
VMRWheels BimmerPost Supporting Vendor 2080 Rep 25,980 Posts Drives: BMW Join Date: Jun 2007 Location: Anaheim, CA iTrader: (4) Garage List 2013 BMW M3 [10.00] 2015 BMW M4 [0.00] 2013 BMW F30 [0.00] 2014 BMW F22 [0.00] 2013 BMW F06 [0.00]	The crack is likely to come back at some point or another. __________________ VMR\|Wheels \| 714.442.7916 \| sales@velocitymotoring.com \| www.velocitymotoring.com \| facebook \| flickr \| Instagram
	Appreciate 0 Quote

07-22-2013, 04:24 PM	#3
spiike32 Major 83 Rep 1,127 Posts Drives: Mineral White F80 M3 Join Date: Apr 2009 Location: IL iTrader: (9)	A more detailed answer is it depends. If the crack is parallel to how the wheel is spinning (like on the barrel, then it should not be welded. Also if there is more than 1 crack it should not be welded. If the crack is on the barrel and crosses the 90* flange then the crack can be opened up, end of the crack drilled out so it doesn't keep cracking, and welded. Some say integrity is just as strong some say it is not. Real world scenario: most likely it will be just fine.... just ugly because you can see the weld beads. If you track and put the wheels to harsher stresses than normal use.. I would not weld them. __________________ Current: Tesla Model 3 Performance Retired: F80 M3, FBO 335i, 318ti, C7 Stingray
	Appreciate 0 Quote

07-22-2013, 04:42 PM	#4
junitos Banned 28 Rep 385 Posts Drives: T0PL3SS BIMM3R Join Date: Nov 2012 Location: VVest Coast iTrader: (1)	Not very long
	Appreciate 0 Quote